Scientists from the University of New South Wales published a report into passivated emitter and rear contact (PERC) and tunnel oxide passivated contact (TOPCon) solar modules, finding that the latter has endured \u201csignificant degradation\u201d in damp heat testing.<\/p>\n
The results of the study were published in the report, \u2018Buyer aware: Three new failure modules in TOPCon modules absent from PERC technology\u2019. The researchers tested a range of both TOPCon and PERC modules, with varying components, such as polyolefin elastomer and ethyl-vinyl acetate, to determine how exposure to damp heat environments could affect the modules\u2019 performance.<\/p>\n
They found that variations in components made little difference to the performance of the modules in this environment, but that the use of TOPCon versus PERC technology made a significant difference. Over 1,000 hours of testing in damp heat environments, PERC modules endured a maximum power loss of just 1-2% relative, compared to a much higher, and wider-ranging, power loss of 4-65% relative in TOPCon modules.<\/p>\n
The team suggested that \u201celectrochemical reactions involving moisture\u201d were likely to blame for the poor performance among TOPCon modules, with three types of failures observed among TOPCon modules: point-localised failure, failure at the connection point of ribbons and busbars and failure throughout \u201cthe whole area of cells [and] modules\u201d.<\/p>\n
While the researchers noted that the specific contaminant responsible for this decline in output is \u201cunclear at present\u201d, they speculated that the presence of sodium and chlorine on solar modules, transmitted from human fingertips during assembly and transportation, could have an effect on TOPCon cell, which were \u201cfound to be particularly vulnerable\u201d.<\/p>\n
This could be a significant development as TOPCon modules are expected to become more commonplace in the global solar sector. Vitor Rodrigues, technical director of Iberia and Latin America at GCL SI, spoke at the 2024 Large Scale Solar Europe summit in London in May, and announced that \u201cPERC will start to disappear\u201d in 2024 as developers shift their focus from PERC to other technologies, such as TOPCon.<\/p>\n
\u201cUrgent and extensive research efforts are crucial to substantially increase our comprehension and fortify the reliability of TOPCon cells against the pernicious effects of moisture and other contaminants,\u201d wrote the researchers in the report, highlighting the importance of further research into the performance of TOPCon modules in humid environments.<\/p>\n